ECP 99

Chemical Mould Release Agent for Concrete Formwork


Description

ECP 99 is specially formulated blend of mineral oils and speciality chemicals having release properties which are superior to those of conventional mould oil. The chemicals react with the alkali in the concrete to form a thin water repellent skin on the surface of the mould, thereby enabling easy stripping mould from concrete and acting as a protection to steel and wooden form-work. ECP 99 is supplied as a ready to use clear low viscosity liquid for direct application and use.


Uses

It is used on most types of form-work to give an optimum release and quality of surface finish to concrete over a wide range designs. Supplied ready to use and can easily be applied by sprayers, squeegee or brush. Need not be thinned


Features

  • Provides a clean positive release even in intricate and difficult casting condition.
  • Reduces labour cost, cleaning time and possible damages to the form-work.
  • ECP 99 assists production of uniform mat stain-free concrete surface with reduced incidents of blow holes and surface blemishes.
  • ECP 99 is unaffected by strong sunlight, drying winds and foot traffic and can be applied to damp form-work.
  • On account of the high rate of coverage the applied cost of ECP 99 compares favorably with that of conventional mould oil. Having regard to the technical benefits additionally obtained, the overall economy of using ECP 99 can be significant.
  • Pockets of air, trapped on the shuttered faces of the concrete, are a major cause of imperfections, necessitating remedial work. The hydrophobic surface produced by chemical reaction between ECP 99 and cement repels surplus water at the interface of the mould and by protecting the concrete from its effect preserves uniformity of surface texture and colour.
  • Due to its excellent release properties, little or no deposit of cement paste remains on the shutter surface.

EFS 99

Heavy Duty Solvent Free Epoxy Floor Screed


Description

EFS 99 is a high build three pack epoxy floor screed system with high chemical and abrasion resistance property. It provides non-dusting, easily cleaned, non slipping floor.


Uses

EFS 99 is seamless protective floor topping used in industries with medium to high vehicular traffic like power plants, exhibition halls, shops, pharmaceutical & fertilizer industries, laboratories, bakeries, super-markets, show rooms, bottling plants, warehouses, breweries, garages, machine shops, chemical plants, dairies, hospitals, refineries, subways, electronics & computer industries, etc. In areas where high degree of cleanliness is required EFR 99 shall be used as top coat with desired colour finish.


Features

  • High mechanical strength, hard wearing and durable
  • Very high Bond and Adhesive strength.
  • Good abrasion resistance
  • Chemical resistance – mostly industrial chemicals
  • Self-leveling, smooth, glossy and hygienic seamless surface
  • High impermeability
  • Does not support bacterial growth.
  • Easy to clean.

Application

Surface Preparation
A sound, clean and dry substrate is absolutely essential for successful coating application and in ensuring maximum bonding between the substrate and flooring system. Floor should be made dry (not more than 5% surface moisture) clean and free from laitance, dust, grease, paint, etc. by scrubbing followed by thorough water wash and wire brushing and then air drying. As the case may be, light sand blasting detergent wash and /or acid etching may also be done. The choice of surface preparation should be determined by the nature and extent of contaminants present on the concrete surface. Damaged or uneven areas, cracks etc. should be made good.

Mixing
suitable power driven mixer / stirrer is recommended for uniform mixing of the EFS 99. Stir the base and hardener separately. Mix hardener gradually into the base under continuous stirring as per the stated mixing ratio. Continue the mixing for 3-4 minutes. Mix the aggregates into the mixed resin portion uniformly under continuous mechanical agitation. Mix well for 5-6 minutes till the components become homogeneous.

Application
The product shall be spread by a notched/smooth steel trowel to the required thickness. The entire mixed material should be placed on to the primed surface (use ICO – 21P Primer) and spread slowly and evenly. Ensure proper leveling and full compaction of freshly laid screed. While application, the substrate temperature should be at least 5°C but not above 500C. Ensure all existing expansion joints are continued through the EFS 99.


Technical Data

  • Appearance of harden screed :- Closed textured even finish
  • Colour :- Off white
  • Mixing ratio :- Pack A: Pack B: Pack C = 2 :1: 11 by weight
  • Specific Gravity :- 1.8±0.2
  • Application Temperature :- Minimum +5°C
  • Coverage (Theoretical) :- 1.8kg /mm thickness
  • Pot life at 27˚C :- 45 minutes for 1kg mass.
  • Tack free time at 27˚C :- 4±1 hours
  • Initial cure at 270C, for pedestrian traffic :- After 24 hours
  • Full cure :- 7 days
  • Flash Point :- Base - Not less than 28°C, Hardener - Not less than 28°C
  • Shelf Life :- 24 Months

EFR 99

Self Leveling Floor Epoxy


Description

EFR 99 is a solventless three pack self leveling epoxy floor topping system with high chemical and abrasion resistance property. It provides non-dusting, easily cleaned, coloured glossy surface.


Uses

EFR 99 is seamless protective floor topping used in industries with medium to high vehicular traffic like power, plants, exhibition halls, shops, pharmaceutical & fertilizer industries, buildings, laboratories, bakeries, super-markets, show rooms, bottling plants, warehouses, breweries, garages, machine shops, chemical plants, dairies, hospitals, refineries, subways, electronics & computer industries etc.


Features

  • High mechanical strength, hard wearing and durable
  • Very high Bond and Adhesive strength.
  • Good abrasion resistance
  • Chemical resistance – mostly industrial chemicals
  • Self-leveling, smooth, glossy and hygienic seamless surface
  • High impermeability
  • Does not support bacterial growth.
  • Easy to clean.

Application

Surface Preparation
A sound, clean and dry substrate is absolutely essential for successful coating application and in ensuring maximum bonding between the substrate and flooring system. Floor should be made dry (not more than 5% surface moisture) clean and free from laitance, dust, grease, paint, etc. by scrubbing followed by thorough water wash and wire brushing and then air drying. As the case may be, light sand blasting detergent wash and /or acid etching may also be done. The choice of surface preparation should be determined by the nature and extent of contaminants present on the concrete surface. Damaged or uneven areas, cracks etc. should be made good.

Mixing
suitable power driven mixer / stirrer is recommended for uniform mixing of the EFS 99. Stir the base and hardener separately. Mix hardener gradually into the base under continuous stirring as per the stated mixing ratio. Continue the mixing for 3-4 minutes. Mix the aggregates into the mixed resin portion uniformly under continuous mechanical agitation. Mix well for 5-6 minutes till the components become homogeneous.